點擊圖片查看大圖
注塑成型
預處理
干燥推薦，如果樹脂中水分含量超過建議水平
干燥溫度=80°C
干燥時間，除濕機=2-4小時
處理含水率=<0.2％
處理
熔體溫度適=295℃
熔體溫度范圍=285-305°C
模具溫度適=100°C
模具溫度范圍=70-120°C
大螺桿切向速度：0.15米/秒
前流速度：150毫米/秒
保持壓力：85兆帕
保持壓力范圍：50?100兆帕
背壓：低
保壓時間：2.5秒/mm
大保持時間：15分鐘
| Rheological properties | dry / cond | Unit | Test Standard | |
| Viscosity number | 150 / * | cm³/g | ISO 307, 1157, 1628 | |
| Moulding shrinkage, parallel | 0.7 / * | % | ISO 294-4, 2577 | |
| Moulding shrinkage, normal | 1.2 / * | % | ISO 294-4, 2577 |
| Mechanical properties | dry / cond | Unit | Test Standard | |
| Tensile Modulus | 5500 / 3500 | MPa | ISO 527-1/-2 | |
| Stress at break | 120 / 75 | MPa | ISO 527-1/-2 | |
| Strain at break | 3 / 13 | % | ISO 527-1/-2 | |
| Flexural Modulus | 4800 / 2900 | MPa | ISO 178 | |
| Flexural Strength | 190 / 100 | MPa | ISO 178 | |
| Tensile creep modulus | ISO 899-1 | |||
| 1h | * / 3300 | MPa | ||
| 1000h | * / 2200 | MPa | ||
| Charpy impact strength | ISO 179/1eU | |||
| 23°C | 40 / 70 | kJ/m² | ||
| -30°C | 40 / 30 | kJ/m² | ||
| Charpy notched impact strength | ISO 179/1eA | |||
| 23°C | 5 / 6 | kJ/m² | ||
| -30°C | 4.5 / 4 | kJ/m² | ||
| -40°C | 4.5 / 4 | kJ/m² | ||
| Izod notched impact strength | ISO 180/1A | |||
| 23°C | 4.5 / 4 | kJ/m² | ||
| -30°C | 4.5 / 3 | kJ/m² | ||
| -40°C | 4.5 / 3 | kJ/m² | ||
| Izod impact strength | ISO 180/1U | |||
| 23°C | 40 / 55 | kJ/m² | ||
| -30°C | 35 / 28 | kJ/m² |
| Thermal properties | dry / cond | Unit | Test Standard | |
| Melting temperature, 10°C/min | 262 / * | °C | ISO 11357-1/-3 | |
| Glass transition temperature, 10°C/min | 80 / - | °C | ISO 11357-1/-2 | |
| Temp. of deflection under load | ISO 75-1/-2 | |||
| 1.8 MPa | 238 / * | °C | ||
| 0.45 MPa | 258 / * | °C | ||
| Vicat softening temperature, 50°C/h, 50N | 205 / * | °C | ISO 306 | |
| Coeff. of linear therm. expansion, parallel | 40 / * | E-6/K | ISO 11359-1/-2 | |
| Coeff. of linear therm. expansion, normal | 96 / * | E-6/K | ISO 11359-1/-2 | |
| RTI, electrical, 0.8mm | 125 / * | °C | UL 746B | |
| RTI, impact, 0.8mm | 120 | °C | UL 746B | |
| RTI, strength, 0.8mm | 125 | °C | UL 746B |
| Flammability | dry / cond | Unit | Test Standard | |
| Burning Behav. at 1.5mm nom. thickn. | HB / * | class | IEC 60695-11-10 | |
| Thickness tested | 1.5 / * | mm | IEC 60695-11-10 | |
| Burning Behav. at thickness h | HB / * | class | IEC 60695-11-10 | |
| Thickness tested | 0.7 / * | mm | IEC 60695-11-10 | |
| Oxygen index | 24 / * | % | ISO 4589-1/-2 | |
| Glow Wire Flammability Index, 0.75mm | 650 / - | °C | IEC 60695-2-1/2 | |
| Glow Wire Flammability Index, 1.5mm | 650 / - | °C | IEC 60695-2-1/2 | |
| Glow Wire Flammability Index, 3mm | 800 / - | °C | IEC 60695-2-1/2 | |
| Glow Wire Ignition Temperature, 0.75mm | 675 / - | °C | IEC 60695-2-1/3 |
| Electrical properties | dry / cond | Unit | Test Standard | |
| Relative permittivity | IEC 60250 | |||
| 100Hz | 3.9 / - | - | ||
| 1MHz | 3.2 / - | - | ||
| Dissipation factor | IEC 60250 | |||
| 100Hz | 130 / - | E-4 | ||
| 1MHz | 150 / - | E-4 | ||
| Volume resistivity | 1E14 / - | Ohm*m | IEC 60093 | |
| Surface resistivity | * / 1E15 | Ohm | IEC 60093 | |
| Electric strength | 25 / - | kV/mm | IEC 60243-1 | |
| Electric Strength, Short Time, 2mm | 25 / - | kV/mm | IEC 60243-1 |
| Other properties | dry / cond | Unit | Test Standard | |
| Humidity absorption, 2mm | 2.2 / * | % | Sim. to ISO 62 | |
| Water absorption, 2mm | 7.6 / * | % | Sim. to ISO 62 | |
| Density | 1230 / - | kg/m³ | ISO 1183 | |
| Water Absorption, Immersion 24h | 1.7 / * | % | ASTM D 570 |
| VDA Properties | Value | Unit | Test Standard | |
| Burning rate, Thickness 1 mm | 27 | mm/min | ISO 3795 (FMVSS 302) | |
| Emission of organic compounds | 6 | µgC/g | VDA 277 |
Chemical Media Resistance
| Acids | |
 |
Acetic Acid (5% by mass) (23°C) |
|
Citric Acid solution (10% by mass) (23°C) |
|
Lactic Acid (10% by mass) (23°C) |
 |
Hydrochloric Acid (36% by mass) (23°C) |
|
Nitric Acid (40% by mass) (23°C) |
|
Sulfuric Acid (38% by mass) (23°C) |
|
Sulfuric Acid (5% by mass) (23°C) |
|
Chromic Acid solution (40% by mass) (23°C) |
| Bases | |
|
Sodium Hydroxide solution (35% by mass) (23°C) |
|
Sodium Hydroxide solution (1% by mass) (23°C) |
|
Ammonium Hydroxide solution (10% by mass) (23°C) |
| Alcohols | |
|
Isopropyl alcohol (23°C) |
|
Methanol (23°C) |
|
Ethanol (23°C) |
| Hydrocarbons | |
|
n-Hexane (23°C) |
|
Toluene (23°C) |
|
iso-Octane (23°C) |
| Ketones | |
|
Acetone (23°C) |
| Ethers | |
|
Diethyl ether (23°C) |
| Mineral oils | |
|
SAE 10W40 multigrade motor oil (23°C) |
|
SAE 10W40 multigrade motor oil (130°C) |
|
SAE 80/90 hypoid-gear oil (130°C) |
|
Insulating Oil (23°C) |
| Standard Fuels | |
|
ISO 1817 Liquid 1 - E5 (60°C) |
|
ISO 1817 Liquid 2 - M15E4 (60°C) |
|
ISO 1817 Liquid 3 - M3E7 (60°C) |
|
ISO 1817 Liquid 4 - M15 (60°C) |
|
Standard fuel without alcohol (pref. ISO 1817 Liquid C) (23°C) |
|
Standard fuel with alcohol (pref. ISO 1817 Liquid 4) (23°C) |
|
Diesel fuel (pref. ISO 1817 Liquid F) (23°C) |
|
Diesel fuel (pref. ISO 1817 Liquid F) (90°C) |
|
Diesel fuel (pref. ISO 1817 Liquid F) (>90°C) |
| Salt solutions | |
|
Sodium Chloride solution (10% by mass) (23°C) |
|
Sodium Hypochlorite solution (10% by mass) (23°C) |
|
Sodium Carbonate solution (20% by mass) (23°C) |
|
Sodium Carbonate solution (2% by mass) (23°C) |
|
Zinc Chloride solution (50% by mass) (23°C) |
| Other | |
|
Ethyl Acetate (23°C) |
|
Hydrogen peroxide (23°C) |
|
DOT No. 4 Brake fluid (130°C) |
|
Ethylene Glycol (50% by mass) in water (108°C) |
|
1% nonylphenoxy-polyethyleneoxy ethanol in water (23°C) |
|
50% Oleic acid + 50% Olive Oil (23°C) |
|
Water (23°C) |
|
Water (90°C) |
|
Phenol solution (5% by mass) (23°C) |
Symbols used:
possibly resistantDefined as: Supplier has sufficient indication that contact with chemical can be potentially accepted under the intended use conditions and expected service life. Criteria for assessment have to be indicated (e.g. surface aspect, volume change, property change).
not recommended - see explanationDefined as: Not recommended for general use. However, short-term exposure under certain restricted conditions could be acceptable (e.g. fast cleaning with thorough rinsing, spills, wiping, vapor exposure).