Polymer; Thermoplastic; ABS Polymer
|
||
| Material Notes: |
LNP STAT-KON* AX00756 is a compound based on ABS resin containing Stainless Steel. Added feature of this material is: Electrically Conductive.
|
||
| Vendors: | No vendors are listed for this material. Please click here if you are a supplier and would like information on how to add your listing to this material. | ||
|
|||
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.16 g/cc | 0.0419 lb/in3 | ISO 1183 |
| 1.165 g/cc | 0.04209 lb/in3 | ASTM D792 | |
| Moisture Absorption | 0.300 % | 0.300 % | 23°C / 50% RH; ISO 62 |
| 0.350 % | 0.350 % | 50% RH, 24 hrs; ASTM D570 | |
Linear Mold Shrinkage, Flow 
|
0.0070 cm/cm @Time 86400 sec |
0.0070 in/in @Time 24.0 hour |
ASTM D955 |
|
0.0070 cm/cm @Time 86400 sec |
0.0070 in/in @Time 24.0 hour |
ISO 294 | |
|
Linear Mold Shrinkage, Transverse
|
0.0078 cm/cm @Time 86400 sec |
0.0078 in/in @Time 24.0 hour |
ISO 294 |
|
0.0080 cm/cm @Time 86400 sec |
0.0080 in/in @Time 24.0 hour |
ASTM D955 | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 28.0 MPa | 4060 psi | ISO 527 |
| 29.0 MPa | 4210 psi | ASTM D638 | |
| Tensile Strength, Yield | 29.0 MPa | 4210 psi | ASTM D638 |
| 30.0 MPa | 4350 psi | ISO 527 | |
| Elongation at Break | 1.8 % | 1.8 % | ASTM D638 |
| 5.4 % | 5.4 % | ISO 527 | |
| Elongation at Yield | 1.7 % | 1.7 % | ISO 527 |
| 1.8 % | 1.8 % | ASTM D638 | |
| Tensile Modulus | 2.58 GPa | 374 ksi | 1 mm/min; ISO 527 |
| 2.96 GPa | 429 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 58.0 MPa | 8410 psi | ISO 178 |
| 61.0 MPa | 8850 psi | ASTM D790 | |
| Flexural Modulus | 2.57 GPa | 373 ksi | ISO 178 |
| 2.84 GPa | 412 ksi | ASTM D790 | |
| Izod Impact, Notched | 0.420 J/cm | 0.787 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 2.08 J/cm | 3.90 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 4.00 kJ/m2 | 1.90 ft-lb/in2 | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 14.0 kJ/m2 | 6.66 ft-lb/in2 | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 8.00 J | 5.90 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Electrical Properties | Metric | English | Comments |
| Surface Resistance | 10 ohm - 1e+05 | 10 ohm - 1e+05 | ASTM D257 |
| Thermal Properties | Metric | English | Comments |
|
CTE, linear, Parallel to Flow
|
69.8 μm/m-°C @Temperature -40.0 - 40.0 °C |
38.8 μin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
|
69.8 μm/m-°C @Temperature -40.0 - 40.0 °C |
38.8 μin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
|
CTE, linear, Transverse to Flow
|
75.5 μm/m-°C @Temperature -40.0 - 40.0 °C |
41.9 μin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
|
75.6 μm/m-°C @Temperature -40.0 - 40.0 °C |
42.0 μin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 93.0 °C | 199 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
|
91.0 °C @Thickness 3.20 mm |
196 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 82.0 °C | 180 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
|
80.0 °C @Thickness 3.20 mm |
176 °F @Thickness 0.126 in |
||