點擊圖片查看大圖
UL rated HB as of 10/97. 200 series recommended when V-2 rating required. Nonhalogenated. 17.5 MFR, for small, intricate parts. Internal mold release.
| You may also be interested in: | ||
| Enhanced Property/特性 | Data Sheet | |
| Improved UV | SLX1231T |
|
| Improved Ductility | EXL1112 |
|
| Improved Ductility | EXL1112T |
|
| Improved HDT（熱變形溫度） | XHT4141 |
|
| Improved HDT（熱變形溫度） | 4301 |
|
| Medical Grade | HP2 |
|
|
Property/特性
|
| TYPICAL PROPERTIES (1) | |||
|
MECHANICAL/機械性能
|
Value/值 | Unit/單位 | Standard/標準 |
|
Tensile Stress, yld, Type I / 抗張程度,屈服,類型I, 50 mm/min
|
62
|
MPa
|
ASTM D 638
|
|
Tensile Stress, brk, Type I / 抗張程度,斷裂,類型I, 50 mm/min
|
68
|
MPa
|
ASTM D 638
|
|
Tensile Strain, yld, Type I / 拉伸伸長,屈服,類型I, 50 mm/min
|
7
|
%
|
ASTM D 638
|
|
Tensile Strain, brk, Type I / 拉伸伸長,斷裂,類型I, 50 mm/min
|
125
|
%
|
ASTM D 638
|
|
Flexural Stress, yld / 撓曲強度, 屈服 , 1.3 mm/min, 50 mm span
|
96
|
MPa
|
ASTM D 790
|
|
Flexural Modulus / 撓曲模量, 1.3 mm/min, 50 mm span
|
2340
|
MPa
|
ASTM D 790
|
|
Hardness，Rockwell / 洛氏硬度 M
|
70
|
–
|
ASTM D 785
|
|
Hardness，Rockwell / 洛氏硬度 R
|
118
|
–
|
ASTM D 785
|
|
Taber Abrasion / 泰伯磨耗量, CS-17, 1 kg
|
10
|
mg/1000cy
|
ASTM D 1044
|
|
IMPACT/沖擊性能
|
Value/值 | Unit/單位 | Standard/標準 |
|
Izod Impact, unnotched / 無缺口懸臂梁沖擊, 23°C
|
3204
|
J/m
|
ASTM D 4812
|
|
Izod Impact, notched / 懸臂梁缺口沖擊強度, 23°C
|
694
|
J/m
|
ASTM D 256
|
|
Tensile Impact Type / 拉伸沖擊值，類型”S”
|
546
|
kJ/m2
|
ASTM D 1822
|
|
Falling Dart Impact / 落錘沖擊 (D 3029), 23°C
|
169
|
J
|
ASTM D 3029
|
|
Instrumented IMPACT Energy @ peak / 儀表控制抗沖擊能量 @ 峰值, 23°C
|
62
|
J
|
ASTM D 3763
|
|
Izod Impact, unnotched / 無缺口懸臂梁沖擊 80*10*3 +23°C
|
NB
|
kJ/m2
|
ISO 180/1U
|
|
Izod Impact, unnotched / 無缺口懸臂梁沖擊 80*10*3 -30°C
|
NB
|
kJ/m2
|
ISO 180/1U
|
|
Izod Impact, notched / 懸臂梁缺口沖擊強度 80*10*3 +23°C
|
65
|
kJ/m2
|
ISO 180/1A
|
|
Izod Impact, notched / 懸臂梁缺口沖擊強度 80*10*3 -30°C
|
11
|
kJ/m2
|
ISO 180/1A
|
|
Charpy（簡支梁缺口沖擊強度） 23°C, V-notch（V型切口） Edgew 80*10*3 sp=62mm
|
65
|
kJ/m2
|
ISO 179/1eA
|
|
Charpy（簡支梁缺口沖擊強度） -30°C, V-notch（V型切口） Edgew 80*10*3 sp=62mm
|
12
|
kJ/m2
|
ISO 179/1eA
|
|
Charpy（簡支梁缺口沖擊強度） 23°C, Unnotch（無缺口） Edgew 80*10*3 sp=62mm
|
NB
|
kJ/m2
|
ISO 179/1eU
|
|
Charpy（簡支梁缺口沖擊強度） -30°C, Unnotch（無缺口） Edgew 80*10*3 sp=62mm
|
NB
|
kJ/m2
|
ISO 179/1eU
|
|
THERMAL/熱性能
|
Value/值 | Unit/單位 | Standard/標準 |
|
Vicat Softening Temp, Rate / 維卡軟化溫度，等級 B/50
|
154
|
°C
|
ASTM D 1525
|
|
HDT（熱變形溫度）, 0.45 MPa, 6.4 mm, unannealed （未退火）
|
137
|
°C
|
ASTM D 648
|
|
HDT（熱變形溫度）, 1.82 MPa, 6.4 mm, unannealed （未退火）
|
129
|
°C
|
ASTM D 648
|
|
CTE（線形膨脹系數）, -40°C to 95°C, flow（流動）
|
6.84E-05
|
1/°C
|
ASTM E 831
|
|
Specific Heat / 比熱
|
1.25
|
J/g-°C
|
ASTM C 351
|
|
Thermal Conductivity / 導熱系數
|
0.25
|
W/m-°C
|
ASTM C 177
|
|
Relative Temp Index, Elec / 相對熱指數， 電性能
|
130
|
°C
|
UL 746B
|
|
Relative Temp Index, Mech w/impact / 相對熱指數，機械沖擊性能
|
130
|
°C
|
UL 746B
|
|
Relative Temp Index, Mech w/o impact / 相對熱指數，非機械沖擊性能
|
130
|
°C
|
UL 746B
|
|
PHYSICAL/物理性能
|
Value/值 | Unit/單位 | Standard/標準 |
|
Specific Gravity / 比重
|
1.2
|
–
|
ASTM D 792
|
|
Specific Volume / 比容
|
0.83
|
cm3/g
|
ASTM D 792
|
|
Density / 密度
|
1.19
|
g/cm3
|
ASTM D 792
|
|
Water Absorption / 吸水率, 24 hours
|
0.15
|
%
|
ASTM D 570
|
|
Water Absorption，equilibrium / 吸水率，平衡, 23C
|
0.35
|
%
|
ASTM D 570
|
|
Water Absorption，equilibrium / 吸水率，平衡, 100°C
|
0.58
|
%
|
ASTM D 570
|
|
Mold Shrinkage / 收縮率, flow（流動）, 3.2 mm
|
0.5 – 0.7
|
%
|
SABIC Method
|
|
Melt Flow Rate / 熔流率,, 300°C/1.2 kgf
|
17.5
|
g/10 min
|
ASTM D 1238
|
|
OPTICAL/光學性能
|
Value/值 | Unit/單位 | Standard/標準 |
|
Light Transmission / 透光率
|
88
|
%
|
ASTM D 1003
|
|
Haze / 霧度
|
1
|
%
|
ASTM D 1003
|
|
Refractive Index / 折射指數
|
1.586
|
–
|
ASTM D 542
|
|
ELECTRICAL/電氣性能
|
Value/值 | Unit/單位 | Standard/標準 |
|
Volume Resistivity / 體積電阻率
|
>1.E+17
|
Ohm-cm
|
ASTM D 257
|
|
Dielectric Strength, in air / 介電強度，空氣中, 3.2 mm
|
14.9
|
kV/mm
|
ASTM D 149
|
|
Relative Permittivity / 相對介電常數, 50/60 Hz
|
3.17
|
–
|
ASTM D 150
|
|
Relative Permittivity / 相對介電常數, 1 MHz
|
2.96
|
–
|
ASTM D 150
|
|
Dissipation Factor / 耗散因素, 50/60 Hz
|
0.0009
|
–
|
ASTM D 150
|
|
Dissipation Factor / 耗散因素, 1 MHz
|
0.01
|
–
|
ASTM D 150
|
|
Hot Wire Ignition / 熱絲引燃 {PLC)
|
2
|
PLC Code
|
UL 746A
|
|
High Voltage Arc Track Rate / 高電壓電弧起痕速率 {PLC}
|
2
|
PLC Code
|
UL 746A
|
|
High Ampere Arc Ign, surface / 高電流電弧引燃，表面 {PLC}
|
1
|
PLC Code
|
UL 746A
|
|
Comparative Tracking Index / 相比耐漏電起痕指數 (UL) {PLC}
|
2
|
PLC Code
|
UL 746A
|
|
FLAME CHARACTERISTICS/火焰特性
|
Value/值 | Unit/單位 | Standard/標準 |
|
UL Recognized, 94HB Flame Class Rating / 阻燃等級 (3)
|
0.71
|
mm
|
UL 94
|
|
Radiant Panel Listing / 輻射板清單
|
YES
|
–
|
UL Tested
|
|
UV-light, water exposure/immersion / 紫外線暴露，耐水/浸漬
|
F2
|
–
|
UL 746C
|
|
Source GMD, last updated:01/04/2000
|
|
Processing/加工方法
|
| Parameter | ||
|
Injection Molding/注塑參數
|
Value/值 | Unit/單位 |
|
Drying Temperature / 干燥溫度
|
120
|
°C
|
|
Drying Time / 干燥時間
|
3 – 4
|
hrs
|
|
Drying Time (Cumulative) / 干燥時間（累積的）
|
48
|
hrs
|
|
Maximum Moisture Content / 大含濕量
|
0.02
|
%
|
|
Melt Temperature / 熔體溫度
|
280 – 305
|
°C
|
|
Nozzle Temperature / 注嘴溫度
|
275 – 300
|
°C
|
|
Front – Zone 3 Temperature / 前區3溫度
|
280 – 305
|
°C
|
|
Middle – Zone 2 Temperature / 中區2溫度
|
270 – 295
|
°C
|
|
Rear – Zone 1 Temperature / 后區1溫度
|
260 – 280
|
°C
|
|
Mold Temperature / 模具溫度
|
70 – 95
|
°C
|
|
Back Pressure / 背壓
|
0.3 – 0.7
|
MPa
|
|
Screw Speed / 螺桿速度
|
40 – 70
|
rpm
|
|
Shot to Cylinder Size / 每次注射量占料筒熔膠總量的百分比
|
40 – 60
|
%
|
|
Vent Depth / 排氣孔深度
|
0.025 – 0.076
|
mm
|
免責聲明：（1）以上所展示的信息由企業自行提供，內容的真實性、準確性和合法性由發布企業負責，環球塑化網對此不承擔任何保證責任。我們原則上建議您優先選擇“塑企通”會員合作! （2）同時我們鄭重提醒各位買/賣家，交易前請詳細核實對方身份，切勿隨意打款或發貨，謹防上當受騙。如發現虛假信息，請向環球塑化網舉報。